品名:镍铬合金 | 牌号:incoloy 907 | 产地:上海 |
镍含量:30% | 货号:13671561267 | 杂质含量:1% |
粒度:5目 |
INCOLOY? alloy 907 (UNS N19907) is a nickel-ironcobalt alloy having high strength along with a low coefficient of thermal expansion. The alloy isstrengthened by age-hardening heat treatments. Table 1 lists the chemical composition of the alloy. The combination of low expansion and highstrength makes INCOLOY alloy 907 useful for gasturbine components. The low expansion enables closer control of clearances and tolerances for greater fuel efficiency. The high strength makes possible higher strength-to-density ratios for lower weight in aircraft engines. For those reasons, INCOLOY alloy 907 is used for gas-turbine seals, shafts, casings, and other structural parts. The properties of INCOLOY alloy 907 are attractive for other applications including instrumentation, glass-to-metal sealing, ceramicmolding dies, and electricity generation. Table 1 - Limiting Chemical Composition, % Nickel ..........................................................................35.0-40.0 Cobalt..........................................................................12.0-16.0 Iron ...............................................................................Balance* Niobium...........................................................................4.3-5.2 Titanium...........................................................................1.3-1.8Aluminum......................................................................0.2 max. Silicon..........................................................................0.07-0.35 Table 2 - Physical & Thermal Properties Density, lb/in3 .....................................................................0.301 Mg/cm3 ...................................................................8.33 Melting Range, °F .....................................................2440-2550 °C .....................................................1335-1400 Specific Heat, Btu/lb-°F ....................................................0.103 J/kg-°C.......................................................431 Curie Temperature, °F ...................................................750-850 °C ..................................................400-455 Thermal Conductivity at 200°F (93°C), Btu-in/ft?-h-°F............................................108.5 W/m- °C ......................................................15.6 Electrical Resistivity, ohm circ mil/ft.....................................419 ??-m .........................................................0.697 Young’s Modulus, 103ksi ....................................................23.9 GPa...............................................................165 Shear Modulus, 103 ksi .........................................................8.8GPa.................................................................61 Poisson’s Ratio....................................................................0.36 Physical Properties Some physical properties of INCOLOY? alloy 907 are listed in Table 2. The values were determined for agehardened material. Values for modulus of elasticity were determined dynamically and were used to calculate Poisson’s ratio. Values were determined at room temperature unless otherwise noted. The composition of INCOLOY alloy 907 is designed to provide a low coefficient of thermal expansion that remains constant over a broad temperature range. As shown in Figure 1, coefficient of expansion is typically 4.0 to 4.5 x 10-6/°F (7.2 to 8.1 x 10-6/°C) at temperatures to about 800°F (430°C). The expansion rate is about half that of other alloys of comparable strength. Further, the expansion characteristics of alloy 907 are highly reproducible after both static and cyclic exposure to temperature. INCOLOY alloy 907 has a nearly constant modulus of elasticity over temperature ranges from the cryogenicregion to 1200°F (650°C). Table 3 lists modulus values at various temperatures. Testing was done on agehardened material using a dynamic method. The combination of low expansion and constant modulus makes INCOLOY alloy 907 highly resistant to thermal fatigue and thermal shock. The alloy’s hightemperature performance is also enhanced by relatively high thermal conductivity. °C Poisson’s Ratio °FTemperature Table 3 - Modulus of Elasticity of Age-Hardeneda INCOLOY alloy 907 a Age hardened for rupture-limited applications 70 200 400 600 700 800 900 1000 1200 14001600 21 93 204 316 371 427 482 538 649 760 871 23.9 23.8 23.8 24.0 24.1 24.3 24.2 23.9 23.0 21.8 20.5 165 164 164 165 166 168 167 165 159 150 141 8.8 8.78.7 8.9 9.0 9.1 9.0 8.8 8.4 8.0 7.4 61 60 60 61 62 63 62 61 58 55 51 0.36 0.37 0.37 0.35 0.34 0.34 0.34 0.36 0.36 0.36 0.39 Young’s Modulus Shear Modulus 10 GPa 3 ksi 10 GPa 3 ksi *Reference to the ‘balance’ of an alloy’s composition does not guarantee this is exclusively of the element mentioned, but that itpredominates and others are present only in minimal quantities.
Incoloy800,NS111,N08800,Alloy800,GH20,1.4876,NCF800供应商
Incoloy800,NS111,N08800,Alloy800,GH20,1.4876,NCF800物理性能:
密度: 7.95 g/cm3 熔点: 1357-1385°C
弹性模量: 196N/mm2 热导率:12.8 λ/(W(m?℃)
硬度: 热膨胀系数( 24 -100°C): 14.2m/m °C
工作温度约量: -200 至 +1,100°C
Incoloy800合金的主要化学成分如下:C≤0.10 Si≤1.0 Mn≤1.5 S≤0.015 Cr=19.0~23.0 Ni=30.0~35.0 Fe≥39.5 Al=0.15~0.6 Ti=0.15~0.6 Cu≤0.75
品种规格有:锻件、棒材、板材、带材、环件、丝材、螺栓、弹簧等协商供应,可根据客户要求生产。
欢迎新老客户来电洽谈咨询,
联系方式:
联系人:罗经理
手机: 13671561267
电话: 021-54461707/021-54192998-618
传真: 021-54192997
QQ: 279851675
邮箱: 279851675@qq.com
上海宝缘钢铁有限公司生产供应Incoloy800H(NS112),无缝钢管、圆钢、管件、锻件、法兰、焊丝、配件等,并可定做各种非标材料。Incoloy800H,又称 NS112 为抗氧化性介质,耐腐蚀,抗高温抗渗碳热强度高,具有优良的机械性能和抗腐蚀性能、加工性能及焊接性能,是具有广泛用途的耐综合腐蚀性能较好的合金。耐蒸汽、软水、蒸汽-空气-CO3混合物,各种酸溶液、盐类、H2S腐蚀。 Incoloy 800H
Incoloy 800H 的化学成分
合金 % 镍 铬 铁 碳 锰 硅 铜 硫 铝 钛
800 最小 30 19 0.15 0.15
35 23 余量 0.10 1.5 1 0.75 0.015 0.60 0.60
800H 最小 30 19 0.05 0.15 0.15
35 23 余量 0.10 1.5 1 0.75 0.015 0.60 0.60
800HT 最小 30 19 0.06 0.15 0.15
35 23 余量 0.10 1.5 1 0.75 0.015 0.60 0.60
铝+钛为0.85-1.20
Incoloy 800H 的物理性能
密度 8.0 g/cm3
熔点 1350-1400 ℃
Incoloy 800H 在常温下合金的机械性能的最小值
合金 抗拉强度 Rm N/mm2 屈服强度 RP0.2N/mm2 延伸率 A5 %
800 500 210 35
800H 450 180 35
特性:
Incoloy 800H和800HT为一双重验证之铁镍铬合金,具800合金之基本化学成分,惟因控制其碳、铝及钛含量及高温退火处理,800H/800HT合金巨幅提高其蠕变断裂强度。低碳含量亦加强其耐应力断裂特性,添加铝及铁则提高其耐高温强度。Incoloy 800H 和800 HT 都是镍铁铬合金,因含有 铝, 碳和钛成份, 该合金有很高的抗拉强度, 高强度的结果接近控制碳、铝、钛含量与高温退火.
应用领域:
用于化工、石油化工加工、发电厂,电站超热油管、加热器、工业炉窑和热处理设备等领域.
Incoloy800,NS111,N08800,Alloy800,GH20,1.4876,NCF800供应商
Incoloy800,NS111,N08800,Alloy800,GH20,1.4876,NCF800物理性能:
密度: 7.95 g/cm3 熔点: 1357-1385°C
弹性模量: 196N/mm2 热导率:12.8 λ/(W(m?℃)
硬度: 热膨胀系数( 24 -100°C): 14.2m/m °C
工作温度约量: -200 至 +1,100°C
Incoloy800合金的主要化学成分如下:C≤0.10 Si≤1.0 Mn≤1.5 S≤0.015 Cr=19.0~23.0 Ni=30.0~35.0 Fe≥39.5 Al=0.15~0.6 Ti=0.15~0.6 Cu≤0.75
品种规格有:锻件、棒材、板材、带材、环件、丝材、螺栓、弹簧等协商供应,可根据客户要求生产。